產品詳情
SA387GR22CL2現貨/SA387GR22CL2價格/SA387GR22CL2切割加工
|
SA387Gr11CL2 |
10 |
2300 |
12000 |
|
SA387Gr11CL2 |
10 |
2300 |
12000 |
|
SA387GR22CL2 |
10 |
2300 |
12000 |
|
SA387GR22CL2 |
6 |
2200 |
12000 |
|
SA387GR22CL2 |
8 |
2000 |
8650 |
|
SA387GR22CL2 |
8 |
2300 |
10700 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
20 |
2200 |
12000 |
|
SA387GR22CL2 |
8 |
2300 |
12000 |
|
SA387GR22CL2 |
12 |
2500 |
12000 |
|
SA387GR22CL2 |
12 |
2500 |
12000 |
|
SA387GR22CL2 |
12 |
2500 |
12000 |
|
SA387GR22CL2 |
16 |
2500 |
12000 |
|
SA387GR22CL2 |
16 |
2500 |
12000 |
四、SA387GR22CL2化學成分：
鋼板的化學成分應符合表1的規定： Wt% 表1
成分
C
Si
Mn
P
S
Cr
V
Mo
Nb
熔煉分析
0.05~0.15
≤0.10
0.30~0.60
≤0.010
≤0.005
2.00~2.50
≤0.010
0.90~1.10
≤0.010
成品分析
0.04~0.15
≤0.10
0.25~0.63
≤0.010
≤0.005
1.95~2.60
≤0.010
0.87~1.13
≤0.010
Al
Ni
Cu
Ti
Sb*
Sn*
As*
[H]*
N*
O*
≤0.06
≤0.20
≤0.15
≤0.010
≤0.003
≤0.010
≤0.012
≤2PPm
≤80PPm
≤30PPm
≤0.06
≤0.25
≤0.15
≤0.010
≤0.003
≤0.010
≤0.012
≤2PPm
≤80PPm
≤30PPm
鋼板厚度/mm
抗拉強度σb(Mpa)
屈服強度σs(Mpa)
伸長率A/%
溫度/℃
沖擊吸收能量KV2/J
180°彎曲試驗 彎曲直徑（b≥35mm）
6-150
520-680
≥310
≥19
20
≥34
d=3a
注： ⑴*分析結果只做記錄，不作驗收條件。
⑵熔煉分析按爐、成品分析按逐軋制張取樣檢驗。
⑶回火脆化敏感性系數應滿足以下要求： X=(10P+5Sb+4Sn+As)×10≤15PPm 式中元素以PPm含量代入，如0.01%應以100PPm代入。 J=(Si+Mn)(P+Sn)×10≤100 式中元素以其百分含量代入,如0.15%應以0.15代入。 P+Sn≤0.012%
五、SA387GR22CL2力學性能：
一、SA387GR22CL2簡介：
適用范圍 本技術條件適用于厚度≤150mm的臨氫設備用SA387Gr22CL2(2 1/4Cr-1Mo)鋼板的生產。
二、SA387GR22CL2執行標準：
美標：ASTM ASME鋼板的尺寸、外形、重量及允許偏差應符合ASME SA387/SA387M標準之規定。
三、SA387GR22CL2交貨狀態：
鋼板以正火（保證貝氏體組織≥90%的加速冷卻 速度）+回火狀態交貨，正火溫度不得超過968℃，回火溫度不得低于720℃。 舞陽鋼廠生產此種材質鋼板