Dual Shield 9000-C1 is an all-b flux cored electrode which produces a 2.5% Ni deposit. The analysis is very similar to the Dual Shield T-90C1 except that this product has out-of-b capability. Dual Shield 9000-C1 is used for welding of 2-3% Ni steels and castings used in applications requiring good toughness at subzero temperatures. Shielding gas 100% CO2and 75%
Ar - Remainder CO2 may be used.
典型拉伸性能
| Condition | 保護氣體 | 屈服強度 | 延伸率 | 抗拉強度 |
| As Welded | 75% Ar - 25% CO2 | 610 MPa | 24 % | 680 MPa |
| As Welded | 100% CO2 | 580 MPa | 25 % | 665 MPa |
夏比V型缺口沖擊性能
| Condition | 保護氣體 | 沖擊值 | 測試溫度 |
| As Welded | 75% Ar - 25% CO2 | 33 ft-lb | -40 °C |
焊縫金屬分析
| 75% Ar - 25% CO2 | 100% CO2 |
| 0.011 % | 0.010 % |
熔敷數據
| 保護氣體 | 安培 | 效率 (%) | 熔敷率 | 電壓 V | 直徑 | 送絲速度 |
| 75% Ar - 25% CO2 | 150 A | 86 % | 1.91 kg/h | 28 V | .045 in. | 200 in./min |
| 75% Ar - 25% CO2 | 210 A | 86 % | 6.3 lb/h | 29 V | .045 in. | 300 in./min |
| 75% Ar - 25% CO2 | 250 A | 87 % | 3.86 kg/h | 30 V | .045 in. | 1016 cm/min |
| 75% Ar - 25% CO2 | 290 A | 87 % | 10.7 lb/h | 33 V | .045 in. | 1270 cm/min |
| 75% Ar - 25% CO2 | 330 A | 87 % | 12.7 lb/h | 34 V | .045 in. | 1524 cm/min |
| 75% Ar - 25% CO2 | 155 A | 87 % | 2 kg/h | 25 V | .052 in. | 150 in./min |
| 75% Ar - 25% CO2 | 245 A | 86 % | 3.31 kg/h | 28 V | .052 in. | 250 in./min |
| 75% Ar - 25% CO2 | 310 A | 85 % | 10.2 lb/h | 33 V | .052 in. | 350 in./min |
| 75% Ar - 25% CO2 | 360 A | 85 % | 13.3 lb/h | 36 V | .052 in. | 1143 cm/min |
| 75% Ar - 25% CO2 | 430 A | 87 % | 17.6 lb/h | 37 V | .052 in. | 1524 cm/min |
| 75% Ar - 25% CO2 | 190 A | 87 % | 2.77 kg/h | 27 V | 1.6 mm | 150 in./min |
| 75% Ar - 25% CO2 | 300 A | 87 % | 10.2 lb/h | 30 V | 1.6 mm | 250 in./min |
| 75% Ar - 25% CO2 | 365 A | 86 % | 12.3 lb/h | 33 V | 1.6 mm | 300 in./min |
| 75% Ar - 25% CO2 | 410 A | 88 % | 14 lb/h | 33 V | 1.6 mm | 350 in./min |
| 75% Ar - 25% CO2 | 450 A | 87 % | 16 lb/h | 33 V | 1.6 mm | 016 cm/min |
| 75% Ar - 25% CO2 | 500 A | 87 % | 20.1 lb/h | 39 V | 1.6 mm | 1270 cm/min |
| 分類: | ASME SFA 5.36, ASME SFA 5.29, E91T1-M21A4-Ni2, AWS A5.36, E91T1-C1A4-Ni2, AWS A5.36, E91T1-Ni2C/Ni2M, AWS A5.29 |